Good Quality Heat Shrinkable Sleeve (2 layers), which are developed and manufacture by Qingdao Huashida machinery Co., Ltd for anti-corrosion of pipeline, are the composition of radiation cross-linked polyethylene backing and high shearing strengthen melt adhesive, and have the function of shape memory. The hot melt adhesive is squeezed into the joint by the shrink power to form a perfectly sealed surface, after being heated. HSSC-1 is compatible with standard pipe coating, also can be used for coating bare, replacement pipe section and large radius bends. The system is designed to be applied with minimum preheating and is ideal for large diameter wastewater pipe.

Feature
Fast shrinkage speed, good waterproof performance, good anti-corrosive performance, long service life, convenient transportation and fast construction. The product are ideal material for corrosion prevention and insulation.

Application scope
It's mainly used for heat pipe network, steel pipe corrosion resistance and insulation, chemical pipes and sewage pipes etc.


Heat Shrinking Wrap

Selecting the proper sleeve:
Project specifications and local standards must be considered when specifying a shrinkable sleeve.
Next to these the following parameters must be considered for selecting the proper shrinkable sleeve:

Pipe Coating Type:
F. I. Bitumen, Coal Tar Enamel (CTE), Cold Applied Tapes (CAT), Fusion Bonded Epoxy (FBE), PolyEthylene (PE), PolyPropylene (PP), ...

Pipe Operating Temperature:
0 - 120° C (0-248° F)
Pipe Operating Pressure:
F. I. 100 mbar = 1, 42 psi, >4 bar = 56.88 psi, ...

Pipe Medium:
F. I. Gas, water, oil, ...

Pipe Diameter:
F. I. 1" or DN25 for steel pipe, 160 mm jacket diameter for insulated steel pipe, ...

Pipe Preparation:
Surface cleaning: F. I. Abrading, brushing, gritblasting obtainable preheat temperature: Low (60-70° C) (140-158° F), high (80-100° C)(176-212° F), very high (230° C) (446° F)
Adverse Soil Conditions:
Stable: Low soil stresses unstable: Shifting soil conditions, significant pipe motion relative to soil
Mechanical Resistance Heatshrinkable Coating:
Medium (B): Moderate impact and penetration resistance high (C): High impact and penetration resistance

Pipe Laying Method:
F. I...Open Trench, Directional Drilling, Off-Shore Climate conditions (Ambient Temperature during Sleeve Application):
Sea climate: Not very cold - not very warm
Land climate: Very cold - warm
Desert climate: Very cold - hot

All of the above parameters affect the type of coating which will provide the best performance, ease of installation and value. The following selection tables will help you to decide which sleeve is right for your application

	ITEM	Standard	UNIT	Data
Adhesive	softening point	ASTM E 28	°C	70-80
	shear strength	DIN 30 672	N/cm	≥100
Basic	specific density	ASTM D792	r/cm 3	0.935-0.96
	tensile strength	ASTM D638	Mpa	15-20
	Elongation at break	ASTM D792	%	350
	hardness	ASTM D2240	ball	48
Heat Shrinkable Sleeve	peel strength	ASTM D1000	N/cm	>150
	water-intake rate	ASTM D570	%	0.05

Construction Case

Oil & Gas Pipe

MRP Pipe

Patent

Client case

Heat Shrinkable Sleeve Production Line

If you have the intention, Please contact us.Welcome you visit
Huashida Machinery, with over 14 years' experience, is one of the professional good quality heat shrinkable sleeve manufacturers in China. Offering the customized service, we warmly welcome you to get the high qualified products from our factory.

	ITEM	Standard	UNIT	Data
Adhesive	softening   point	ASTM   E 28	°C	70-80
	shear strength	DIN   30 672	N/cm	≥100
Basic	specific   density	ASTM   D792	r/cm   3	0.935-0.96
	tensile strength	ASTM   D638	Mpa	15-20
	Elongation at break	ASTM   D792	%	350
	hardness	ASTM   D2240	ball	48
Heat Shrinkable Sleeve	peel   strength	ASTM   D1000	N/cm	>150
	water-intake rate	ASTM   D570	%	0.05